Mold Max™ STROKE

  • Brushable Silicone

Mold Max™ STROKE is a brushable tin silicone rubber that self-thickens for making fast brush-on moulds of almost any model. Properly applied, it will hold a vertical surface and will reproduce the finest detail. Mixed 100A:10B by weight, rubber quickly develops thixotropy and can be applied with a brush or spatula. Working time is 30 minutes, re-coat time is 45 minutes and cure time after the final layer has been applied is 16 hours at room temperature.

Mold Max™  STROKE - Brushable Silicone

Quick Tech Data

  • 100A:10B

    Mix Ratio By Weight

  • 30 minutes

    Pot Life

  • 16 hours

    Cure Time

  • White


  • 30 A

    Shore Hardness

Mold Max™  STROKE - Brushable Silicone

Mold Max™ STROKE silicone will not stick to most surfaces and will cure with negligible shrinkage to a strong, flexible Shore 30A rubber. 4 thin layers is all that is necessary to make a strong and durable production mould for casting wax, gypsum, concrete or resins (urethane, polyester, etc.). Applications include reproducing sculpture, architectural restoration, candle moulds, etc.

Available Sizes

  • Trial Kit
    *Vat Included
  • Net Wt: 1 kg
  • Gallon Kit
    *Vat Included
  • Net Wt: 4.99 kg

Product Questions

Total 1 question(s) page: 1

How can I eliminate bubbles from my castings?

Question submitted by: username | on: date time

Using a vacuum chamber or pressure pot will help in removing most to all bubbles from your castings. You can read more here.

Answer submitted by: username | on: date time